Abstract
AbstractPoly(ethylene‐co‐vinyl alcohol) (EVOH) hollow fiber membranes were prepared by thermally induced phase separation (TIPS) process. Water, methanol, and acetone were used to extract the diluents in the fibers, respectively. Bigger shrinkage of fibers during extractant evaporation was observed when water or methanol was used. Their interaction parameters with EVOH were calculated via Hansen solubility, respectively. The mechanism of hollow fiber volume shrinkage was discussed. It was found that affinity of the extractant with polymer was the critical factor except for the surface tension of extractant. Through the X‐ray diffraction analysis during extraction and evaporation, the crystallization behavior of the polymer was studied. From the SEM photos, it was observed that the volume shrinkage was derived from the collapse of porous structure. The fiber sample extracted by acetone had similar morphology with the sample freeze‐dried. The gas and water permeability were also measured and the results were coincident with the morphology of fibers and shrinkage data. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 4106–4112, 2007
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.