Effect of polymer blend types and gamma radiation on the physico-chemical properties of polycarbonate

Abstract

ABSTRACTSamples from polycarbonate (PC) were classified into two main groups. The first group was blended with Abietic acid (Rosin) with different compositions, while the second group was blended with ethylene-vinyl acetate (EVA) copolymer with almost the same composition. A comparative study of the effect of both Rosin and EVA concentration on the thermal stability of PC has been investigated using thermogravimetric analysis. The results show that blending with Rosin causes the dominance of degradation. Samples from PC with 20% Rosin blend were irradiated with gamma at the dose of range 20–300 kGy. The resultant effect of gamma radiation on the structural properties of the 20% Rosin/ 80%PC blend has been investigated using Fourier Transform Infrared FTIR spectroscopy. The results indicate that degradation of the polymer blend dominates, thus increases the creation of hot free radicals that leads to the formation of color centers in PC. In addition, the transmission of the 20% Rosin/80%PC samples as well as color changes was studied. The color intensity ΔE was greatly increased with increasing the gamma dose up to 300 kGy, accompanied by a significant increase in the blue color component.