Abstract
In this study a range of wholly aromatic copolyesters based on kink m‐acetoxybenzoic acid (m‐ABA) monomer (33 mol%) and equimolar‐linear p‐acetoxybenzoic acid (p‐ABA), hydroquinone diacetate (HQDA) and terephthalic acid (TPA) monomers (67 mol%) have been synthesized by melt polycondensation reaction process at 280°C and 260°C for different time intervals. Characterization of copolyesters were performed by solution viscosity measurement, wide–angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC), hot‐stage polarized light microscopy, proton‐nuclear magnetic resonance analysis (1H‐NMR). According to the results obtained, copolyesters showed thermotropic liquid crystalline behavior in an appropriate temperature range. The copolyesters were prepared in high yields. It was observed that the intrinsic viscosities of the copolyesters are increased regularly with increasing polymerization time and temperature. All the copolyesters were soluble in a trifluoroacetic acid/dichloromethane (30:70 v/v) except the copolyesters which were synthesized at 280°C in 5 h. According to the WAXD results; the degree of crystallinity of copolyesters were found to be between 5–15%. DSC and hot stage polarized light microscopy results showed that all the copolyesters are melt processable and a significant molecular interaction exist in a very broad temperature range (160°C and 165°C) in the nematic mesophase. The Tg values are increased with an increasing polycondensation reaction time and temperature and they were observed between 93–126°C. Fibers prepared by a hand‐spinning technique from the polymer melt exhibit well‐developed fibrillar structure parallel to the fiber axis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.