Effect of poly(acrylic acid) on the preparation of thick silica films by electrophoretic sol–gel deposition of re-dispersed silica particles

Abstract

Thick silica films were prepared by the electrophoretic sol–gel deposition technique in the presence of poly(acrylic acid) (PAA) using monodispersed silica particles; the particles were prepared by the sol–gel method, pre-heat treated and then re-dispersed in the mixture of H2O and ethanol. The weight of deposited silica films was maximized when 0.2 mass % of PAA against the whole amount of sol was added. The particles constructing the thick silica films were packed densely when the amount of added PAA was less than 0.2 mass%. The weight of the film increased with decrease in the content of H2O in the sol when a fixed amount of PAA was added. After the heat treatment of deposited films at 800 °C, crack-free silica films of about 30 μm thickness were prepared. © 1998 Chapman & Hall