Abstract
Edible film made from water-soluble fish proteins present in surimi wash-water were developed based on formulation conditions explored in a previous study. Type and concentration of plasticizer significantly ( p < 0.05) affected the mechanical and barrier properties of the films. Sorbitol (SOR) plasticized films were the most brittle, with the highest tensile strength (TS, 3.14MPa) however its effect on water vapour permeability (WVP) was low (30.41g/mm/m2/d/kPa). In contrast, glycerol (GLY) and polyethylene glycol (PEG) plasticized films exhibited flexible structure despite a low TS (2.13MPa and 1.80MPa, respectively) resulting in higher WVP (125.8g/mm/m2/d/kPa and 89.52g/mm/m2/d/kPa). As plasticizer concentration increased, TS decreased concomitant with an increase in elongation as break (E) and higher WVP. SOR plasticized films, showed higher film solubility (FS) and protein solubility (PS) compared to GLY and PEG plasticized films. Increasing the plasticizer concentration, overall, resulted in both higher FS and PS. The colour of films was more affected by the nature of the plasticizer used than by its concentration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.