Abstract
This article presents the effects of pineapple leaf (PALF), napier, and hemp fibres as filler on the scratch resistance of epoxy composites. In particular, it explores the effect of these natural fillers on the horizontal load, coefficient of friction (COF), penetration depth, fracture toughness, scratch hardness, brittleness index and scratch observation. The mixing method using magnetic stirrer was used to produce the natural fibre-filled epoxy composites with different wt%, namely, 5, 7.5, and 10wt%. The test was performed using a CSM Revetest Xpress, which consisted of a cone of the half-apex angle of 60° ending with a sphere having a tip radius of 200μm. The indenter scratch distance and speed were 7mm and 1.5mm/min, respectively. The results show that the napier fibre-filled epoxy composites have the highest peak load and COF. It was also noted that the napier fibre-filled epoxy composites have the lowest penetration depth for each wt% of filler. Lastly, the fracture toughness (Kc) for the napier fibre-filled epoxy composites with 10wt% of filler yielded the highest value of 4.33MPa.m1/2. It can also be seen that using a scanning electron microscope (SEM), the amount of debris increased with higher of wt% of the natural fibre fillers in the composites. Hence it was demonstrated that the napier fibre-filled epoxy composites have higher scratch resistance compared to the PALF and hemp fibre-filled epoxy composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.