Abstract
The effects of phosphoric acid (H3PO4) in pressurized aqueous solution on the dehydration of CaSO4·2H2O to form α-hemihydrate gypsum (α-HH) phase and the regulation of crystal shape were studied in this paper in order to provide guidance for the low-cost and high-value utilization of phosphogypsum. The results showed that H3PO4 can significantly accelerate the formation rate of the α-HH phase and that it did not participate in the formation of the α-HH phase in the form of eutectic phosphorus during crystalline phase transformation. In terms of crystal shape regulation, H3PO4 can impact the effect of a citric acid crystal regulator on α-HH crystal shape regulation. The more H3PO4 added, the greater the aspect ratio of α-HH. Accordingly, the water consumption and 2 h dry compressive strength of α-HH products were gradually increased and decreased with an increase in H3PO4 content, respectively. Despite this, the compressive strength of α-HH can still meet the requirements of the α20 grade in JC/T 2038-2010 "α High Strength Gypsum" in China when the H3PO4 content was limited to less than 0.4%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.