Abstract
Multiphasic calcium phosphate powders were synthesized by the acidic route, using lactic acid as a chelating agent that allows the production of a stable and rich solution of calcium and phosphate ions at room temperature. After pH adjusting, without varying the concentrations of precursor solution, XRD and FTIR analyses showed different CaP phases before and after heat treatment at 1000 °C. At pH 5, brushite plate-like particles were produced, while at higher pH levels (7 to 12) nano-hydroxyapatite particles were formed. After the calcination process, partial and total decomposition of hydroxyapatite in the β-TCP phase was explained by XRF analysis due to the calcium-deficient hydroxyapatite of synthesized samples at pH 7 and 10. This work presents an important method to synthesize any desired CaP phase compositions by varying the pH level and subsequently performing heat treatment, which has a direct effect on morphology, crystallinity, and formation of different CaP powders.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.