Abstract
In this study, Ni–Al2O3 metal matrix composite (MMC) coatings were prepared from a modified Watt's type electrolyte by pulse current (PC) plating under current densities varying between 1 and 9A/dm2. The tribological tests were performed with a reciprocating ball-on-disk apparatus sliding against a M50 steel ball (Ø 10mm). The wear tests were carried out at sliding velocities of 50, 100 and 150mm/s under a constant load. The results compared with our previously published work of DC electrodeposited coatings. The results showed that the electrodeposition method can significantly affect the microstructure and tribological behavior of Ni–Al2O3 nanocomposite coatings. For the same current density, PC electrodeposition creates coatings with higher co-deposited particle content, more homogenous particle distribution, higher wear resistance at high sliding distance and improved friction coefficients. The superior dispersion of Al2O3 nanoparticles in PC-coated materials contributed to its increased load bearing capacity. Detailed tribological tests and characterization showed that DC- and PC-coated nanocomposite layers yielded different wear mechanisms depending on the sliding velocity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.