Abstract
The failure of plasma-sprayed thermal barrier coatings (TBCs) during service or thermal cycle testing usually results from internal cracking in the top coat, erosion and CMAS (calcium-magnesium-alumina-silicate)-induced damage, etc. The microstructure of ceramic coatings affects their durability and other properties of TBCs. In the present study, yttria-stabilized zirconia (YSZ) coatings were deposited by atmospheric plasma spraying (APS) using feedstocks with different particle sizes. In addition, the effect of particle size on damage evolution in the top coat was investigated. It is found that the coatings deposited using coarse particles show the higher thermal cycle life. Crack length grew with increasing numbers of thermal cycles. The faster crack growth rate can be found for the coatings deposited from fine particles. The porosity of the coating made from the coarse powder is larger than the porosity of the coating made from fine powder both in the as-sprayed condition and after thermal cycling. The changes in crack growth rate and the porosity are related to the effect of sintering and stress evolution in coatings during the thermal cyclic tests.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.