Abstract
A quasi-realistic aging test of NCA/graphite lithium-ion 18650 cylindrical cells is performed during a long-term low c-rate cycling and using a new protocol for testing and studying the aging. This to emulate a characteristic charge/discharge profile of off-grid PV-battery systems. The cells were partially cycled at four different cut-off voltages and two state of charge ranges (ΔSOC) for 1000 and 700 cycles over 24 months. Differential voltage analysis shows that a combination of loss of active material (LAM) and loss of lithium inventory (LLI) are the causes of capacity loss. Cells cycled with high cut-off voltages and wide ΔSOC (20% to 95%) were severely affected by material degradation and electrode shift. High cut-off voltage and narrow ΔSOC (65% to 95%) caused greater electrode degradation but negligible cell unbalance. Cell impedance is observed to increase in both cells. Cells cycled with middle to low cut-off voltages and narrow ΔSOC (35%–65% and 20% to 50%) had comparable degradation rates to calendar-aged cells. Cycling NCA/graphite cells with low c-rate and high cut-off voltages will degrade the electrode in the same way high c-rate would do. However, low c-rate at low and middle cut-off voltages greatly decrease cell degradation compared to similar conditions at middle to high c-rate, therefore increasing battery lifetime.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.