Abstract
The influence of P2O5on the properties of alite-calcium strontium sulphoaluminate cement was researched by means of X-ray diffraction, scanning electron microscope-energy dispersive spectroscopy (SEM-EDS) and petrographic analysis. The results show that the optimal content of P2O5is 0.3% and the compressive strength of the cement at 1, 3, 28d are 27.0, 59.1, 110.9MPa when the calcining temperature is 1350°C. P2O5mainly exists in the belite and a suitable amount of P2O5can promote the formation of C1.5Sr2.5A3and alite. When the content of P2O5is higher than 0.3%, the formation of C1.5Sr2.5A3and alite can be hindered. P2O5can enhance the hydration heat evolution rate in the acceleration period and the hydrate heat of cement containing P2O5increases slightly.