Abstract
Gd 2 O 3 thin films were deposited by Ion-beam sputtering (IBS) under the oxygen flow of 0 sccm～30 sccm. The structure and optical properties of the Gd 2 O 3 optical films were investigated by Lambdar950 spectrophotometer, laser calorimetry and atomic force microscopy (AFM). When oxygen flow was less than 10 sccm, with the increase of oxygen flow, the transmittance of the films increased, at the same time absorptance and the surface roughness of the films decreased. While the flow was more than 10 sccm, with the increase of the flow rate, the surface roughness of the films increased, but the transmittance and absorptance did not show any apparent change. The results show that both the structure and optical properties are closely related to the flow of oxygen. XPS measurements demonstrated that when the oxygen flow increase from 0 sccm to 10 sccm, the defect oxygen decreases. But when the oxygen flow increase from 10 sccm to 30 sccm, the defect oxygen increase. The XPS spectra show that when the oxygen flow was 10 sccm, the defect oxygen was the least. Thus when the oxygen flow was 10 sccm, the structure and optical properties of the Gd 2 O 3 optical films were the best.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call