Abstract
AbstractIn this work, the effect of the processing conditions on the thermal behavior of a commercial poly(L‐lactic acid) (PLLA) was investigated. In particular, PLLA having a very high molecular weight was processed by a discontinuous mixer at different mixing conditions. The molar mass variation was investigated by size exclusion chromatography–multiangle laser light scattering chromatography, and the thermal characteristics were detected by the conventional differential scanning calorimetry and dynamic mechanical thermal analysis. Tensile tests were performed at room temperature and at 60°C. Our attention was essentially focused on the crystallization behavior of the various samples obtained. A modest decline in the molar mass was obtained with two mixing temperatures of 210 and 250°C, but a significant increase in the crystalline phase content was noticed, with a concomitant tremendous increment in the crystallization rate. A correlation was also made between the molar mass distribution and crystallization rate in isothermal conditions, where clearly visible were the effects of the processing temperature on both the molar mass distribution and how the nucleating agents affected the crystallinity of PLLA. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.