Effect of nucleating agent on the crystallization of tailings glass ceramics prepared by one-time sintering

Abstract

Glass ceramics was made by the one-time sintering method using the main raw material of iron tailings. On the basis of quaternary system of CaO-MgO-Al2O3-SiO2, using DTA, XRD and SEM, the effects of different nucleating agents and mixing amounts as well as heat treatment on the crystallization of tailings glass ceramics were studied. The experimental results show that, nucleating agent and heat treatment are two necessary conditions for one-time sintering preparation of tailings glass ceramics namely, only adding nucleating agent or experiencing heat treatment, the quaternary system can not crystallize. The composite nucleating agent consisting of Cr2O3 and TiO2 can further lead to the crystallization of the CaO-MgO-Al2O3-SiO2 quaternary system at the lower temperature, with the major phase of diopside. In the range of mass content, 0%–4%, crystal intensity and crystal content grow. But when mass content is more than 4%, the crystal size will become coarser and the crystal distribution will be less regular. Different heat treatment regimes do not change the composition of the crystalline major phase in the glass ceramics crystallization of CaO-MgO-Al2O3-SiO2 system. In the range of 30–60 minutes, with the extension of nucleation and crystallization, crystallization degree enhanced, but if the holding time surpasses 60 minutes, the crystallization is worse.