Abstract

N,N′-Dimethylformamide (DMF) and N,N′-dialicylidene ethylene diamine cobalt(II) (CoSalen) were added into the casting solution to improve both the gas permeability and oxygen/nitrogen selectivity of polycarbonate (PC) membranes. PC membranes formed by a simple dry method are known to have high oxygen/nitrogen selectivity but low gas permeability. A nonsolvent, DMF, was added into the casting solution to improve the membrane permeability, and an oxygen carrier, CoSalen, was added to improve the oxygen/nitrogen selectivity. The addition of DMF increased the membrane permeability but reduced the oxygen/nitrogen selectivity. On the contrary, the addition of CoSalen raised the selectivity but suppressed the permeability. To make a membrane of selectivity near the value of native PC membrane but with a higher gas permeation rate by adjusting the DMF and CoSalen contents in the casting solution, the highest oxygen permeation flux of CoSalen complexed porous PC membranes was 0.61 GPU(10−6 × cm3/cm2.s.cmHg) at an O2/N2 selectivity of 4.7 at 35°C. This membrane was obtained when 19 vol% of DMF and 4.8 wt% of CoSalen were added into the PC casting solution. This specific membrane, after a long period of storage, 400 days, had a higher oxygen flux (0.88 GPU) which was obtained without any loss in selectivity. At a lower temperature, 5°C, an even higher oxygen selectivity of 7.9 was obtained.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.