Abstract
The present study focused on the effect of N in ferritic Fe–9Cr–1Mo and austenitic 304 L alloy substrates on the formation and cyclic oxidation behavior of aluminide coatings fabricated by chemical vapor deposition (CVD). Relatively high N contents in the commercial alloys caused the formation of AlN precipitates in the CVD aluminide coating, which adversely affected the adhesion of the as-deposited coatings, particularly on 304 L. The reduction of N content in the substrate alloys resulted in a cleaner coating layer with fewer precipitates and Kirkendall voids. However, the cyclic oxidation behavior of the aluminide coatings in air + 10 vol.% H 2O at 700 °C was not noticeably changed by the N reduction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.