Abstract
The 10NiO-NiFe2O4 composite ceramics doped with NiO were prepared with the cold isostatic pressing-sintering process. The effects of NiO doping order on the density, bending strength and electrical conductivity of NiFe2O4 composite ceramics were studied. The results show that, doping excess 10wt% NiO before synthesis of NiFe2O4 composite (doping order one) and doping excess 10wt% NiO after synthesis of NiFe2O4 composite (doping order two), the former’s samples have a better relative density 88.9% and linear shrinkage rate 9.82%, which is increased by 7.12% and 3.6% compared with that of latter’s samples, respectively. At the same time, the former’s samples also have a better electric conductivity and reach 1.29S/cm at 1233K, which is higher about 13.15% than those latter’s samples. However, the bending strength of the former’s samples just has 76.28Mpa, which is lower about 15.41% than that of the latter’s samples 88.04Mpa.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call