Abstract
Due to environmental concern, lead-free solder are taking the place of eutectic Sn-Pb solder in electronic packaging industry. Among various lead free alloys, Sn–Ag–Cu (SAC) alloys are leading lead-free candidate solders for various applications because it is offered better properties. This study investigates the interfacial reactions during reflow soldering and isothermal aging between Sn-3.0Ag-0.5Cu (SAC305) and Sn-3.0Ag-0.5Cu-0.05Ni (SACN30505) on electroless nickel/ immersion palladium/immersion gold (ENEPIG) surface finish. The substrates were subjected to isothermal aging at 125°C for up to 2000 hours with solder size diameter of 500μm. The results indicated that after reflow soldering, (Cu, Ni)6Sn5 IMC is formed between solder and substrate while after aging treatment a new IMC was formed between (Cu, Ni)6Sn5 and substrate known as (Ni, Cu)3Sn4. Moreover, after soldering and isothermal aging, Ni-doped (SACN) solder represents a thicker IMC compared to SAC solder. Aging time of solder joints results in an increase of IMC’s thickness and changes their morphologies to become more spherical, dense and with larger grain size. In addition, the results also revealed that the thickness of intermetallics formed is proportional to the aging duration.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.