Abstract
Abnormal tool wear is a significant problem encountered in machining. MoS2 has the function of friction reduction; thus, to mitigate friction, two Ni-based coatings, Ni60 and Ni60 + 15 wt.% Ni/MoS2, were obtained on tungsten steel using supersonic plasma technology. The microstructure, phase structure, microhardness, fatigue properties, and friction and wear properties of the two coatings were characterized. The results show that the two plasma-sprayed Ni-based coatings have desirable structures. The addition of Ni-coated MoS2 can effectively improve the hardness of the coatings, with values reaching as high as 735 HV. The speed of rotation of the friction ball was set as 200 r/min, and the cutting force was 201.6 N. The fatigue performance as well as the friction and wear performance of the coating are simulated using ANSYS. The fatigue performance is improved by 12.6 % after adding 15 wt.% Ni/MoS2, and the friction system of the coating becomes stable after 25 min of contact. The addition of 15 wt.% Ni/MoS2 can effectively improve the performance of the tool material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.