Effect of Ni doping on the structural and magnetic properties of FePt nanoparticles

Abstract

A serial of FePtNi nanoparticles were investigated on their crystal structure and magnetic properties. The FePtNi nanoparticles were synthesized simultaneously by the reduction of iron (III) acetylacetonate, platinum (II) acetylacetonate and nickel (II) acetylacetonate with 1,2-hexadecanediol as the reducing agent. The X-ray diffraction patterns indicate that the addition of 8, 12, 17 at% Ni in FePt nanoparticles suppressed the transformation of the particles from disorder face-centered cubic to order face-centered tetragonal L1 0-phase under annealing treatment. However, further increasing Ni contents to 21 at%, the nanoparticle transformed to L1 2 phase. Doping of Ni into the FePt compound system may decrease coercivity and crystal anisotropy energy. A maximum coercivity of 7 KOe at room temperature was obtained for (Fe 52Pt 48) 92Ni 8 nanoparticles after annealing at 600 °C for 30 min.