Abstract
Pure and co-doped BiFeO3 (Ca, Nd) nanoparticles with diameter in the range of 50–250nm were synthesized through a sol–gel method. X-ray diffraction (XRD) and Raman results show that Bi-site co-doped with Ca, Nd could result in a transition of crystal structure (from single phase rhombohedral (R3c) to two phase coexistence). An apparent blue shift can be observed in the co-doped samples along with a decrease of the direct optical band gap. Moreover, the leakage current was decreased due to the introduction of nonvolatile Ca and Nd at Bi3+ site. Analysis of MPMS-VSM magnetic hysteresis data reveals a further enhancement in magnetism in the Nd doped Bi0.9Ca0.1FeO3, which is further explained by XPS characterization.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.