Abstract
Niobium nitride (NbN) and zirconium nitride (ZrN) were deposited on Ti substrates by direct-current (DC) reactive magnetron sputtering; the deposited NbN and ZrN films served as intermediate layers of a Ti and porcelain interface. X-ray diffraction (XRD) results proved that the deposited NbN and ZrN films were polycrystalline with a cubic microstructure. The Ti and porcelain bonding strength of the samples in Group Control (27.2±0.75MPa), Group NbN (43.1±0.59MPa), and Group ZrN (52.4±0.80MPa) were measured. The surface roughness in the case of Group Control (1.863±0.10μm), Group NbN (2.343±0.07μm), and Group ZrN (2.346±0.10μm) was also investigated. Statistical analysis showed that both films helped improve the Ti and porcelain bonding strength and increase the surface roughness. Scanning electron microscopy (SEM) results showed that no apparent oxide layer was formed at the Ti and porcelain interface in both Group NbN and Group ZrN. Energy-dispersive X-ray spectroscopy (EDS) results showed that ZrN was more effective in preventing Ti oxidation than was NbN. Overall, the experimental results showed that the deposition of both NbN and ZrN films helps improve the Ti and porcelain bonding strength and that ZrN films are more effective.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.