Effect of Nb content variations on the microstructure and mechanical properties of NiCrMo welded joints

Abstract

The effects of varying the Nb content (1.04 wt%-1.55 wt%) in NiCrMo weld metals on the microstructure, tensile strength and cryogenic impact toughness were investigated. The microstructure of the three different weld metals was observed to be composed of austenite matrix and precipitates by characterization techniques such as SEM, EDS, EBSD, and TEM. The precipitates within the grains were NbC and Ni3Nb phases, and the precipitates on the grain boundaries were NbC phases. With the increase of Nb content, the average grain size of austenite decreased from 205.3 μm to 161.4 μm, and the area fraction of precipitates increased from 1.41% to 3.97%. The cryogenic impact value of the welded joints decreased from 97 J to 76.3 J, while the tensile strength increased from 682.5 MPa to 710 MPa, indicating that the increase in the area fraction of the Nb-rich phase had a deleterious effect on the cryogenic impact toughness and was conducive to the elevation of the tensile strength. When the Nb content in the weld metal was 1.25 wt%, the comprehensive mechanical properties of NiCrMo welded joints were the best, with a tensile strength of 695.5 MPa and a cryogenic impact value of 86.7 J.