Abstract
The microstructure and mechanical properties of the CoCrCuFeNiNb high-entropy alloy coating prepared by plasma transferred arc cladding process were investigated. Two phases are found in the prepared coating with Nb: one is face-centered-cubic solid solution phase; the other is the Laves phase of (CoCr) Nb type. The nano-indentation testing indicates that the microhardness (H), elastic modulus (E), the hardness/modulus of elasticity ratio (H/E ratio) and high resistance to plastic deformation (H3/E2) of the coating with Nb are 6.13GPa, 221GPa, 0.028 and 4.7×10−3 respectively. The CoCrCuFeNiNb coating displays excellent wear and corrosion resistance. The wear resistance of the coating with Nb is about 1.5 times higher than that of the coating without Nb under the same wet sand rubber wheel abrasion testing conditions. Compared with the coating without Nb and as-cast 304 stainless steel, the coating with Nb shows the lowest icorr values in polarization curves and the highest fitted Rf values in EIS plots in 6N hydrochloric acid solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.