Abstract
ABSTRACTNiCrBSi coatings with different Nb additions have been prepared by laser cladding. The microstructure, phase composition, hardness, and wear resistance of the coatings were studied by scanning electron microscopy (SEM), electron probe microanalyser (EPMA), X-ray diffraction (XRD), microhardness tester and M-200 wear tester. The results show that the phases in the NiCrBSi coating without Nb addition include γ-Ni, Cr23C6, Cr7C3, Ni3B, Ni3Si2 and CrB. The NbC phase appears in coatings after the addition of Nb element. When the addition of Nb is 2 wt-%, the NbC particles with a size of about 1.2 μm were found in the coating, and the amount of NbC is about 1.8 vol.-%. With the increase of Nb addition, the size and amount of NbC in the coatings also increased. When the addition of Nb is 6 wt-%, the size of NbC is about 2.3–6.1 μm and the morphology of NbC changed from particle to quadrangular and petaloid shaped. In addition, when the addition of Nb is 2 wt-%, the hardness and wear resistance of the coating are the best, and the wear resistance of the coating is 104% higher than that without Nb addition.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.