Abstract
Abstract Different plasma electrolytic oxidation (PEO) coatings were prepared on AZ91D magnesium alloy in electrolytes containing various concentrations of (NaPO 3 ) 6 . The morphologies, chemical compositions and corrosion resistance of the PEO coatings were characterized by environmental scanning electron microscopy (ESEM), X-ray diffractometer (XRD), energy dispersive analysis of X-rays (EDAX), potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) test. The results showed that the PEO coatings were mainly composed of MgO, Mg 2 SiO 4 , MgAl 2 O 4 and amorphous compounds. As the (NaPO 3 ) 6 concentrations increased from 0 to 10 g/l, the thickness and surface roughness of the coatings approximately linearly increased; the MgO and Mg 2 SiO 4 phase increased within the concentration range of 0–3 and 0–5 g/l, and then decreased within the range of 3–10 and 5–10 g/l, respectively, while the MgAl 2 O 4 phase gradually decreased. Moreover, the corrosion resistance of the coatings increased within the range of 0–5 g/l and then decreased within the range of 5–10 g/l. The best corrosion resistance coating was obtained in electrolyte containing 5 g/l (NaPO 3 ) 6 , it had the most compact microstructure. Besides, a reasonable equivalent circuit was established, and the fitting results were consistent with the results of the EIS test.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.