Abstract
Densification and micro-structural development of ultra fine 8 mol% yttria stabilized zirconia (8YSZ) nano powder were investigated systematically by varying the SPS sintering temperature at constant applied pressure of 50 MPa. A hundred fold decrease in average grain size ranging from 10 μm to 80 nm is observed on decreasing the SPS sintering temperature from 1200 °C to 1050 °C with >99% of theoretical densities. Impedance measurements on the samples indicated an enhancement in the ionic conductivity at 700 °C from 0.004 S/cm to 0.018 S/cm with decrease in grain size from 10 μm to 0.51 μm and a significant increase in conductivity from 0.018 S/cm to 0.068 S/cm on further reduction of grain size to 80 nm. A significant change in the grain-boundary conductivity is noticed on reducing the grain sizes to nano regime. The diverse microstructure with ultra fine grain size resulting from SPS at 1050 °C could contribute to the enhanced ionic conductivity, which is supported by the activation energy data.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.