Abstract
The current work studies the electrospun poly (vinyl alcohol) (PVA) nanofibers and its nanocomposites including nanohydroxy apatite (nHAp) and nHAp/cellulose nanofibers (CNFs), emphasizing the impact of nanofillers on the toughness of nanofibers. PVA nanofibers were incorporated with 10 wt% of nHAp and then various amounts of CNF were added to subsequent PVA/nHAp fibrous nanocomposites. The morphology of nonwoven mats was studied by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). While neat PVA nanofibers were smooth and uniform in thickness, the nanofiller loading resulted in thinner fibers with less uniformity. Furthermore, the thermal properties of the nonwoven network of fibers were characterized employing thermogravimetric analysis (TGA). Although the maximum loss mass temperature of PVA was partially reduced upon addition of nanofillers, the onset of decomposition was not altered. The mechanical characterizations were performed using static tensile and dynamic mechanical analysis (DMA). Compared to neat PVA mats, the tensile test of nanocomposites mats demonstrated the significant increase in Young’s modulus; however, strain at break was dramatically reduced. In addition, the fracture work was assessed from the area under the stress-strain curve, which showed brittleness of fibrous nanocomposites due to the nanofiller incorporation. Field emission SEM (FE-SEM) was employed to scan the fracture surface of stretched fibers. The increase in modulus of electrospun mats was also shown by DMA in frequency mode. In parallel, both tensile test and DMA confirmed the change in fracture of PVA fibers from a tough to brittle mode, due to the nanofiller addition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.