Abstract
Abstract The pure and Fe-containing nanocrystalline layers were fabricated on the surface of 2024 Al alloy by surface mechanical attrition treatment (SMAT) using ceramic balls and steel balls, respectively. The friction and wear properties of 2024 Al alloy before and after SMAT were investigated by sliding against a GCr15 steel ball of 5 mm in diameter at a load of 1.5 N. The results demonstrate that the surface nanocrystalline layers with average grain sizes of 49.2 and 52.1 nm can be obtained by using ceramic balls and steel balls, respectively, when treated for 30 min. Moreover, a 5 μm thick surface layer containing Fe is also introduced into the Al nanocrystalline surface when treated using steel balls. The wear resistance of 2024 Al alloy is improved due to the combination of grain refinement, increased hardness and lubrication effect of iron-containing layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.