Abstract

The effect of NaNO3 concentration on the anodic electrochemical behavior of antimony in 4 M NaOH solution was investigated using cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) analyses. The mechanism of NO 3 − concentration effect on the anodic electrochemical behavior of antimony was proposed, and its availability was confirmed by experimental results. The effect of NaNO3 on the anodic behavior of antimony in NaOH solution can be interpreted as a stepwise formation of different antimony compounds with different NaNO3 concentrations. Metallic antimony is apt to be oxidized into Sb2O3 within the NaNO3 concentration range of 0–0.48 M. NaSbO3 can be found on the antimony surface when the NaNO3 concentration increases gradually. Insoluable NaSbO3 inhibits the anodic oxidation of antimony due to its shielding effect on the mass transport of the reactants and products. Surface morphology and composition were analyzed by X-ray photoelectron spectroscopy (XPS), scanning electronic microscopy (SEM), and electron dispersion spectroscopy (EDS) analyses. Results indicate that the anodic oxidation layer is composed of Sb2O3, NaSbO3, and Sb. The atomic proportion of antimony in the form of NaSbO3 increases with increasing NaNO3 concentration due to the powerful oxidizing property of NaNO3.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.