Effect of Nano-Y2O3 on the Microstructure and Properties of Fe-Cr-C-N-Al Surfacing Alloy

Abstract

In this paper, Fe-Cr-C-N-Al-Y wear-resistant surfacing alloy was prepared by open-arc surfacing with self-shielded flux-cored wire. The wear properties of the surfacing alloy were analyzed using an MLS-23 rubber wheel wet sand wear tester. The phase composition and microstructure of the surfacing alloy were analyzed using X-ray diffraction, scanning electron microscope, electron backscatter diffraction and transmission electron microscope; the strengthening mechanism and wear mechanism of the alloy were discussed. The results show that the microstructure of Fe-Cr-C-N-Al-Y surfacing alloy is composed of M + γ-Fe + M7C3 + AlN. When the content of nano-Y2O3 is 0.456 wt.%, the formability of the surfacing alloy is the best, and the wetting angle is the smallest, which is 50.8°; AlN and M7C3 precipitate the most, and the microstructure grain is the smallest. At this time, the hardness value of the surfacing alloy is up to 62.3 HRC, which is 11.8% higher than that of the unmodified surfacing alloy. The minimum wear weight loss is 0.125 g, and the wear resistance is increased by 41.86%. The wear mechanism of the surfacing alloy is mainly a plastic deformation mechanism, and the material removal processes are microcutting and furrow wear. This study provides theoretical guidance for refining primary carbides and improving the wear resistance of high chromium cast iron.