Abstract
Al2O3-C refractory samples were prepared using corundum, flake graphite, Al and Si powders and phenolic resin as raw materials. The in-situ synthesis mechanism of Al5O6N in Al2O3-C refractories was studied and the effect of adding nano metallic Fe on the formation and microstructure of Al5O6N phase was also investigated. Thermodynamic calculations show that Al5O6N can potentially be synthesized in a reducing atmosphere at 1600°C over a narrow range of N2 and CO pressures. Experimental results proved that Al5O6N phase was synthesized after 1600°C heat treatment when nano Fe was added to Al2O3-C refractories. As the content of nano Fe increases, Al5O6N particles show disappearance of oriented growth, with octahedron shapes turning into spherical agglomerations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.