Abstract
CrN coatings were deposited by Closed Filed Unbalanced Magnetron Sputtering (CFUMS). The effect of N2 flow rate on composition, phase components, morphologies and mechanical properties of CrN coatings were studied. The results show that the deposition rate of CrN coatings declined with the increase of nitrogen flow percentage in a Ar/N2 mixture atmosphere. When the nitrogen flow percentage reached 50% or more, the Cr and N atomic ratio of CrN coatings is close to 1:1. The phase in coatings was the coexistence of Cr, Cr2N and CrN, but the crystal preferred orientation changed significantly with the different N2 flow rates. The columnar crystal CrN coating with low N2 flow rate was denser. The hardness and adhension of CrN coatings have no direct relationship with N2 flow rate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.