Abstract
Abstract The high density polyethylene (HDPE)/short glass fiber (SGF) composites were prepared by multistage tensile extrusion with an assembly of laminating-multiplying elements (LMEs) connecting with an extruder. The strong shear and elongational force field in LME could make the fibers orientated along the melt flow direction. The degree of fiber orientation could be controlled by the number of LMEs. The SEM morphological observations illustrated that the fiber orientation degree was gradually increased by increasing the number of LMEs. However, the fiber length distribution and crystallinity of composites did not change much with increasing the LMEs, and would not affect the mechanical properties. The essential work of fracture (EWF) analysis at quasi-static rate of loading showed that the fracture toughness along the melt flow direction increased with the number of LMEs increasing because of the change of the fiber related damage mechanism. An opposite trend was found if samples were stretched perpendicular to the melt flow direction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.