Abstract
This work focuses on the preparation of electrospun Polyvinyl Alcohol (PVA) nanofibres of three different molecular weights. The electrospinning process parameters were varied in terms of the voltage and feed rate. Scanning Electron Microscopy technique was used to characterize the morphological structure of the electrospun PVA nanofibre. The results show that the average fibre diameter increased as the molecular weight of the polymer increased. The formation of beads occurs from the lowest molecular weight sample of 89K However, long, continuous and beaded-free fibres were obtained from the 125K and 205K polymer weight PVA. The results also suggest that higher spinning voltage and feed rate produce larger fibre diameter, respectively.Keywords : Polyvinyl Alcohol, nanofibres, molecular weight, electrospinningCorresponding Author:Khairunnadim Ahmad Sekak, Faculty of Applied Sciences, Universiti Teknologi MARA (UiTM), Shah Alam, 40450 Selangor Darul Ehsan.Email: nadim821@salam.uitm.edu.my
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.