Abstract
Abstract The influence of molar mass of the shell layer of latex particles having core–shell morphology on film-forming and final coating properties of self-crosslinking latexes based on keto-hydrazide crosslinking system was investigated. Structured latex particles were prepared by the semi-continuous non-seeded emulsion polymerization of acrylic monomers. The particle core was slightly crosslinked to prevent the copolymers forming the core phase from migration into the shell phase. The molar mass of copolymers forming the shell phase was gradually reduced by isooctyl 3-mercaptopropionate chain transfer agent included in the synthesis of the shell layers. The results confirmed theoretical predictions and revealed that even a slight amount of chain transfer agent added during the synthesis achieved a substantial lowering of minimum film-forming temperature and reduction of water sensitivity of latex coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.