Abstract
The influence of molybdenum, and molybdenum with niobium addition on the phase transformation behaviour of a developed low-carbon CrNiMnB ultrahigh-strength steels, was investigated. Gleeble 3800 thermomechanical simulator was employed to simulate the hot-rolling process and to get the dilatation curves. After austenitization at 1250 °C for the complete dissolution of carbides, specimens received 0.6 total strain (i.e., 0.2 at 1100 °C and 2 x 0.2 at 900 °C) followed by cooling at various cooling rates (CRs) in the range of 2-60 °C/s. The final microstructures were investigated using laser scanning confocal microscopy, field emission scanning electron microscopy, and hardness measurements. Then the continuous cooling transformation diagrams were constructed based on the dilatation curves, microstructure, and hardness values. The electrolytic extraction method was used to assess the elements' distribution and the composition of the forming precipitates. The addition of Mo increased the hardenability, decreased the transformation temperatures, and promoted the formation of low-temperature transformation products i.e., martensite and bainite ferrite, at different CRs and inhibit the formation of polygonal ferrite. The formation of coarse precipitates neglected the effect of Mo+Nb addition, decreased the hardenability and expanded the region of BF formation to high CRs. The variation in the hardness with microstructural changes was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.