Abstract
Thin films of ZnO and (ZnO: Mn) are grown via chemical spray pyrolysis (CSP) technique Structure analysis of ZnO and ZnO: Mn films were studied via XRD. The results offer that films were cubic with a prevailing peak along (002). The grain size is (10. 45-12. 41) nm, whilst the strain decrease from 31. 68 to 27. 91 with Mn. AFM images assure the creation of nanostructured. It was found that the Average Particle size, average roughness (Ra ) and root mean square rough (Rrms) decreased with an increase of Mn content in ZnO films, Films are transparent in visible area with cut-off wavelength at 370 nm. High transparency is seen at (>85%) in the visible area. Optical bandgap energy decreases from 3. 05 to 2. 95 eV with increase of Mn doping content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.