Effect of Mn Nanoparticles on Interfacial Intermetallic Compound Growth in Low-Ag Sn-0.3Ag-0.7Cu-xMn Solder Joints

Abstract

Interfacial intermetallic compound (IMC) growth between Cu substrates and low-Ag Sn-0.3Ag-0.7Cu-xMn (x = 0 wt.%, 0.02 wt.%, 0.05 wt.%, 0.1 wt.%, and 0.15 wt.%) (SAC0307-xMn) solders was investigated under different isothermal aging temperatures of 100°C, 150°C, and 190°C. Scanning electron microscopy (SEM) was employed to observe the microstructural evolution of the solder joints and measure the IMC layer thickness. The IMC phases were identified by energy-dispersive x-ray spectroscopy and x-ray diffraction. The results showed that a Cu6Sn5 IMC layer formed in the as-soldered solder joints, while a duplex structure consisting of a Cu6Sn5 IMC layer near the solder matrix and a Cu3Sn IMC layer was observed after isothermal aging. A considerable drop in the IMC layer thickness was observed when 0.1 wt.% Mn nanoparticles were added. Beyond this amount, the thickness of the IMC layer only slightly increases. Adding Mn nanoparticles can increase the activation energy and thus reduce the interdiffusion rates of the Sn and Cu atoms, which suppresses excessive IMC growth. The solder joint containing 0.1 wt.% Mn nanoparticles has the highest activation energy. SEM images revealed that the number of small particles precipitated in the channels between the Cu6Sn5 IMC layers increases with an increasing proportion of Mn nanoparticles. Based on the microstructural evolution of the solder joints, this study revealed that grain boundary pinning is one of the most important mechanisms for IMC growth inhibition when Mn nanoparticles are added.