Abstract
Effect of Minor Si and Ag additions on glass-forming ability (GFA) of the base Ti44Cu38.9Co4Zr6Sn2Be5.1(at. %) alloy are studied. (Ti44Cu38.9Co4Zr6Sn2Be5.1)100-xRx(R = Si, Ag, x=0, 1, 2, 3 at. %) metallic glasses are formed by splat-quenching and copper mold suction casting. It is found that the minor Si and Ag additions enhance the glass-forming ability of Ti44Cu38.9Co4Zr6Sn2Be5.1greatly. The maximum size of fully amorphous structure is increased from 4 mm for base alloy to be larger than 6 mm for alloys containing 1-2 at. % Si/Ag, while Si/Ag more than 2 at. % additions decrease the GFA.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.