Abstract
The effect of milling time on consolidation of Al5083-5wt. % nanoyttrium oxide powders which are milled from 0-35 hours using planetary ball mill. nanocrystalline structure was observed after 10hours of milling. X-ray diffraction results reveals the formation of 57nm and 31nm for 20hr and 35hr of milling with increase in lattice strain. Circular and Elliptical morphology of milled powders were confirmed through SEM with decrease in particle size. The 90o die channel angle ECAP die was used to consolidate 20hr and 35hr milled powder aided with and without back pressure. The optical micrographs reveal the formation of fine grains. The35hr milled powder shows the maximum densification of 96% and 20hr milled powder shows maximum hardness of 82HRB was observed in 20hr milled powder. Both are consolidated for two passes in route-A and sintered at 430°C for one hour.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.