Abstract
Polymer composites by and large found suitable for many specific applications in the field of electrical, electronics, marine, aerospace and microelectronics. Thus a new technique for processing polymer composites has been explored and one such is microwave curing. The roles of microwave in the post curing of polymer matrix composites cannot be under estimated, as it has the capacity to improve the mechanical properties of the composite produced. The aim of the study is to determine the effect of microwave post curing on the tensile property of aluminum reinforced and carbon black reinforced unsaturated polyester composites. This effect was compared with that post cured using conventional oven with the objective of investigating the significance of microwave curing on the tensile strength of the produced composites. A specific study comprising of aluminum filled polyester based composite and carbon black filled polyester based composite were investigated using two different composite curing methods (microwave and conventional thermal heating). The investigation, through experimentation was based on mechanical property (tensile strength) of the produced composites. Comparing the results of the post-curing of the composites using microwave and conventional methods, there is direct relationship between the tensile strength and the percentage weight fraction of the fillers with respect to the post curing methods. 30% aluminum filled, post cured in microwave has 0.01 MPa tensile strength, 20% aluminum filled (microwave) has 0.0076MPa while 30% aluminum filled (conventional oven curing) has 0.0092MPa and 20% aluminum filled (conventional oven curing) has 0.0068MPa.It was concluded that post-curing of the particulate composites through microwave is able to improve the tensile strength better as compared to thermal conventional method.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.