Effect of microstructure on media noise of CoCrTa thin film media fabricated under ultra clean sputtering process

Abstract

Ultra clean sputtering process (UC-process) was introduced in the fabrication of Co/sub 85.5/Cr/sub 10.5/Ta/sub 4/Cr thin film media. Magnetic properties, microstructure and their effect on media noise are discussed against the thickness of Cr underlayer. By applying the UC-process, coercive force H/sub c/ shows high values of about 2.3 kOe isotropically until 10 nm in Cr thickness. High H/sub c/ of about 1.5 kOe remains at even 2.5 nm. UC-process is found to enable the enhancement of the formation of Cr segregated grain boundary structure, which reduces intergranular exchange coupling even in the media with 2.5 nm in Cr thickness. The ratio of readback signal to media noise S/Nm gradually increases with decreasing Cr thickness, and shows the highest value at 2.5/spl sim/5 nm. In the media with sufficiently separated grains by segregated grain boundaries, the reduction of the grain size with decreasing Cr thickness is found to be most effective for the improvement of S/Nm.