Abstract
The influence of microstructure and composition on permeation of hydrogen in 1.2 and 0.5 wt.% Mn X70 pipeline steels after different processing was investigated using an electrochemical permeation technique.For 1.2 wt.% Mn (standard Mn) steel, the microstructure of normalised transfer bar was coarse equiaxed ferrite grains. This sample exhibited the highest diffusivity, followed by transfer bar, with a mixed ferrite–bainitic ferrite microstructure; and hot rolled strip, with fine elongated ferrite grains.The 0.5 wt.% Mn (medium Mn) strip displayed lower diffusivity than the 1.2 wt.% Mn strip, due to hydrogen trapping by finer ferrite grains and a higher density of carbonitride precipitates. Moreover, the medium Mn strip exhibited a uniform microstructure and consequently similar diffusion coefficients for the edge and centreline regions, whereas the finer grains of the edge region of the standard Mn strip resulted in a lower diffusivity than the centreline region.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.