Abstract
Sintered bodies of TiO2nanopowders were fabricated by magnetic pulsed compaction (MPC) and subsequent 2 step sintering in this study and then, the effect of micro Ti and P-25 nano TiO2 powder addition on density, shrinkage and hardness was investigated. The optimum processing conditions in order to find the maximum density, hardness and shrinkage were found to be 0.5~0.7 GPa MPC pressure and 1450oC sintering temperature, with addition of 6% of TiO2 P-25 nanopowder. High pressure and rapid compaction using magnetic pulsed compaction (MPC) enhanced the density with increasing MPC pressure up to 0.7 GPa without the formation of surface or edge cracks on the consolidates bulks, and significantly reduced the shrinkage rate (about 15 in this case) of the sintered bulks compared to the general process (about 18%). Overall, most of the properties showed gradual changes with increasing MPC-ed pressure and TiO2 P-25 nanopowder content. Keywords: Densification, magnetic pulsed compaction, mechanical properties, rutile, sintering, TiO2 nanopowder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.