Abstract
Ambiguous fatigue failure mechanism of micro-arc oxidation (MAO) coated samples was an urgent issue to be solved. In this paper, the influence mechanism of coating defects on the fatigue property of the samples with thin MAO coating was studied. Based on the stress analysis of the MAO coated 2024-T3 Al alloy, the effect of the MAO coatings produced using 8%, 10%, 15%, and 20% duty cycles on fatigue behavior was discussed. Fatigue fracture and strain under cyclic stress were measured with SEM and extensometer, respectively. The results showed that the maximum cyclic stress affected the initiation of fatigue cracks. With the increase in the external loading, stress variation of the coatings was the critical issue that caused the changes in the fatigue performance under the high and low cyclic stresses. Furthermore, the fatigue failure mechanism of the samples with the thin MAO coatings was revealed. This study provided a method basis for further exploring the fatigue property of the samples with the thick MAO coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.