Effect of MgO content on the formation and superconducting properties of (Bi,Pb)-2223 phase in the partial-melting and sintering process

Abstract

The bulk samples with the composition Bi 1.8Pb 0.4Sr 1.9Ca 2.1Cu 3.5O y + x wt.% MgO ( x=0, 0.5, 2, 5, 10 and 15) were prepared by sintering at 840°C for 240 h after partial-melting at 875°C for 1 h. The sample with 0.5 wt.% MgO addition shows the lowest melting temperature of Bi-2212 phase and the highest conversion of Bi-2212 phase to Bi-2223 phase. With increasing MgO content, the width of hysteresis loop ΔM of the bulk samples at 77 K increases (0⩽ x⩽5), and then decreases (5⩽ x⩽15). The largest ΔM appears in the sample with 5 wt.% MgO addition. It is suggested that an amount (∼5 wt.%) of MgO addition in the (Bi,Pb)-2223 superconductors can increase J c due to improving the flux pinning. In contrast, MgO overdoping (>5 wt.%) decreases J c due to decreasing the conversion of Bi-2212 phase to Bi-2223 phase.