Abstract
Micro-nanoTiB2 ceramic was prepared through increasing the molar ratio of Mg and leaching with suitable acid by the combustion synthesis reaction of Mg, TiO2 and B2O3, which could get higher temperature and purer product. The Samples were investigated by XRD and SEM, and the results showed the diameter of the TiB2 was 200 nm ~ 300 nm and the shape of the TiB2 was irregular hexagonal crystal. The diameter of the TiB2 was decreased with the increase of Mg powder. The formation mechanism of TiB2 has been studied.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.