Abstract
Pneumatic chipping hammer and ultrasonic impact peening were used to relieve the welding residual stress of 2205 duplex stainless steel by manual argon arc welding, and the influences of these mechanical shock treatment technologies on the residual stress, microstructure, and corro-sion resistance of the welding seam were studied. Results showed that after pneumatic chipping hammer or ultrasonic impact peening, a small amount of plastic deformation occurred in the welded joint of 2205 duplex stainless steel, which led to an increase in the dislocation density in the microstructure. Meanwhile, the stress state of the welded joint changed from the residual tensile stress to the residual compressive stress. The maximum residual compressive stress could reach −579 MPa. The combined action of the two effectively improved the corrosion resistance of the welded joint. Among them, the best overall effect was the ultrasonic impact peening tech-nology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.